PA6 Zytel® 73M30 NC010 DUPONT USA

256

Unit Price:US$ 3,074 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
88.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Easy electroplating
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Enhanced level

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			低翘曲性热稳定性

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level	0.8mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	0.9mm	UL 94	HB
FMVSS flammability		FMVSS302	SE

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	4800 Mpa
tensile strength	Break	ISO 527-2	82.0 Mpa
Bending modulus		ISO 178	4800 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Tensile modulus		ASTM D638/ISO 527	4800 kg/cm²(MPa)[Lb/in²]
Tensile strain	Break	ISO 527-2	15 %
Tensile creep modulus	1hr	ISO 899-1	-- Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	5.7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	6.5E-05 cm/cm/°C
			Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	8.9E-05 cm/cm/°C
				Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	5.6E-05 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO 11359-2	6.3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	221 °C
Vicat softening temperature		ISO 306/B50	210 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	195 °C
Combustibility (rate)		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.1 %
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	6.3 %
Shrinkage rate	MD	ISO 294-4	0.90 %
	Shrinkage rate	TD	ISO 294-4	0.90 %
	Shrinkage rate	Shrinkage rate		ASTM D955	0.9 %
density		ASTM D792/ISO 1183	1.35

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.