Material Properties:high strength｜Creep resistance｜Filler: Glass fiber reinforced material｜50% filler by weight
Application Areas:Automotive interior parts｜sporting goods｜Vehicle electronics｜Lawn and garden equipment｜Application in the automotive field｜Business equipment｜Power/Other Tools｜Home appliance components｜Industrial applications｜furniture｜Electrical enclosure｜Engine parts｜Camera applications｜Electrical appliances｜Shell｜Metal substitution｜Machine/mechanical components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Method	Test Result
Balance, 23 ℃, 50% RH	%	0.70to1.5
23℃,24hr	%	0.16to0.30
Saturation, 23 ℃	%	0.060to0.15
melt mass-flow rate	g/10min	3.6to20
Flow: 23 ℃	mm/mm	38.1E-3-78.7E-3
Melt volume flow rate	ISO 527-2/5	0.01to0.04

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		°C	798to904

Mechanical properties	Test Condition	Test Method	Test Result
Yield, 23 ℃		%	2.0to3.0
Fracture, 23 ℃		%	1.6to2.1
Fracture, 23 ℃	Fracture, 23 ℃			151.72to280.69 MPa

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		J/m	0.222to0.332
Impact strength of simply supported beam without notch		kJ/m²	2.647to20.893

Electrical performance	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)	V
dielectric strength	V/mil	500to840
Surface Resistivity	ohms	5.0E+3-6.0E+15
Volume resistivity	ohms·cm	3.0E+2-2.1E+16

Thermal performance	Test Method	Test Result
horizontal	mm/mm/°C	55.9E-5-50.8E-5
0.45MPa, Not annealed	°C	234to255
1.8MPa, Not annealed	°C	223to230
flow	mm/mm/°C	137.2E-5-25.4E-5

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.