Material Properties:UV resistance｜Easy to process｜High mobility｜High impact resistance
Application Areas:Automotive sector｜Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Method	Test Result
Melt volume flow rate	ISO 1133	30.0 cm3/10min
Shrinkage rate	ISO 294-4	0.80 %
Water absorption rate	ISO 62	1.2 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	103
ball-indentation hardness		ISO 2039-1	86.0 Mpa

Mechanical properties	Test Method	Test Result
tensile strength	ISO 527-2	43.0 Mpa
Tensile strain	ISO 527-2	3.5 %
Flexural modulus	ISO 178	1800 Mpa
bending strength	ISO 178	62.0 Mpa
Tensile modulus	ISO 527-2	2000 Mpa

film	Test Condition	Test Method	Test Result
elongation		ISO 527-3	>50 %

Electrical performance	Test Method	Test Result
Surface Resistivity	IEC 60093	1E+14 ohms
Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
relative permittivity	IEC 60250	2.90
Dissipation Factor	IEC 60250	0.015

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	65.0 °C
vicat		ISO 306/A50	160 °C
vicat	vicat		ISO 306/B50	102 °C
Linear coefficient of thermal expansion		ISO 11359-2	1E-04 cm/cm/°C
Heat distortion temperature		ISO 75-2/B	85.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.