PC/ABS CYCOLOY™ 143R-GY7G036 L10932439 SABIC INNOVATIVE NANSHA
191
- Unit Price:US$ 4,096 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low viscosity｜Weather resistance｜UV resistance
- Application Areas:film｜Wire and cable
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 70 |
| R级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 138 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 132 °C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| vicat | ASTM D15256 | 154 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C | |
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| specific heat | ASTMC351 | 1260 J/kg/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| refractive index | ASTM D542 | 1.586 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.762mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 800 J/m |
| ASTM D1822 | 546 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | -- | ASTM D792 | 1.20 g/cm³ |
| Outdoor applicability | UL 746C | f1 | |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 平衡,23°C | ASTM D570 | 0.35 % | |
| 平衡,100°C | ASTM D570 | 0.58 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| density | -- | ASTM D792 | 1.19 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| 50Hz | ASTM D150 | 9E-04 | |
| 60Hz | ASTM D150 | 9E-04 | |
| dielectric constant | 60Hz | ASTM D150 | 3.17 |
| 1MHz | ASTM D150 | 2.96 | |
| 50Hz | ASTM D150 | 3.17 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.1 Mpa |
| elongation | 断裂 | ASTM D638 | 110 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| tensile strength | 断裂 | ASTM D638 | 65.5 Mpa |
| 屈服 | ASTM D638 | 62.1 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.