Material Properties:Flame retardant｜Hydrolysis resistance｜Low warpage｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Automotive sector｜Laptop case｜Electrical/Electronic Applications
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	217 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	184 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Electrical performance	Test Method	Test Result
volume resistivity	IEC 60093	1E+16 ohms·cm
dielectric strength	IEC 60243-1	18 KV/mm
arc resistance	ASTM D495	93.0 sec
Compared to the Leakage Tracking Index (CTI)	IEC 60112	V

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	TD	ISO 294-4	0.50-0.70 %
shrinkage rate	shrinkage rate	MD	ISO 294-4	0.10-0.30 %

mechanical properties	Test Condition	Test Method	Test Result
flexural modulus	23°C	ISO 178	10400 Mpa
bending strength	23°C	ISO 178	200 Mpa
Tensile modulus		ISO 527-2/1A/1	10700 Mpa
tensile strength	断裂	ISO 527-2/1A/5	140 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	2.0 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.