'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT Cristin® SK608 BK509 DUPONT USA
273
- Unit Price:US$ 3,680 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Automotive Applications｜Electronic and electrical components
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 | kJ/m² |
| -30°C | ISO 179/1eU | 65 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | <100 | mm/min |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | UL 94 | HB | ||
| 0.75mm | UL 94 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Extreme Oxygen Index | ISO 4589-2 | 20 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | ISO 178 | 210 | Mpa | |
| Tensile modulus | ISO 527-2 | 14200 | Mpa | |
| tensile strength | Break | ISO 527-2 | 140 | Mpa |
| Tensile strain | Break | ISO 527-2 | 2.0 | % |
| Bending modulus | ISO 178 | 13300 | Mpa | |
| Tensile stress | 23 ℃, 5 mm/min，Break | ISO 527-1 | 160 | MPa |
| Tensile strain | 23℃，Break | ISO 527-1 | 2.1 | % |
| Tensile modulus | 23℃, 1.0 mm/min | ISO 527-1 | 14300 | MPa |
| bending strength | 23℃ | ISO 178 | 235 | MPa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 207 | °C |
| Vicat softening temperature | ISO 306/B50 | 215 | °C | |
| Melting temperature | ISO 11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 8E-05 | cm/cm/°C |
| MD | ISO 11359-2 | 2E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 222 | °C |
| UL flame retardant rating | 3.00 mm | UL 94 | HB | |
| Linear coefficient of thermal expansion | 平行Flow，23 to 55℃(73 to 130°F) | ISO 11359-1 | 0.000080 | cm/cm/℃ |
| 垂直Flow，23 to 55℃(73 to 130°F) | ISO 11359-1 | 0.000080 | cm/cm/℃ | |
| Hot deformation temperature | 1.8 Mpa，Unannealed | ISO 75A-1 | 205 | ℃ |
| UL flame retardant rating | 0.750 mm | UL 94 | HB | |
| 1.50 mm | UL 94 | HB | ||
| Melting temperature | ISO 3146 | 225 | ℃ | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Top out temperature | 170 | °C | ||
| MediumDensity | 1.47 | g/cm³ | ||
| Shrinkage rate | TD | ISO 294-4 | 1.1 | % |
| MD | ISO 294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 0.30 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.10 | % | |
| Shrinkage rate | Across Flow | ISO 294-4 | 1.3 | % |
| Flow | ISO 294-4 | 0.3 | % | |
| Water absorption rate | 23C/59RH | ISO 62 | 0.1 | % |
| Sat/23C | ISO 62 | 0.3 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the anti leakage trace index | IEC 60112 | PLC 1 | ||
| Dissipation factor | 1MHz | IEC 60250 | 0.013 | |
| 100Hz | IEC 60250 | 3.8E-03 | ||
| Relative permittivity | 1MHz | IEC 60250 | 3.90 | |
| 100Hz | IEC 60250 | 4.10 | ||
| Dielectric strength | IEC 60243-1 | 32 | KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Odor | VDA270 | 3.00 | ||
| EmissionofOrganicCompounds | VDA277 | 70.0 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.