PBT Cristin® HR5315HFS NC010 DUPONT USA
169
- Unit Price:US$ 4,637 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:25MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Easy to form｜Easy to process
- Application Areas:Automotive components｜Electronic and Electrical Applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 200 °C | |
| Glass Transition Temperature | ISO 11357-2 | 65.0 °C | |
| melting temperature | ISO 11357-3 | 225 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 32 mm/min |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| FMVSS flammability | FMVSS302 | B |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 30 kJ/m² |
| 23°C | ISO 179/1eU | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 42 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 250°C,1000sec^-1 | ISO 11443 | 175000 mPa·s |
| Ejection Temperature | 170 °C | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| FlowLength2 | 2.00mm，FlowLength | 400 mm | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.50 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.4 % |
| bending strength | ISO 178 | 145 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.