POM Delrin®  100ST DUPONT SHENZHEN

170
  • Unit Price:US$ 9,031 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    30MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details
  • Material Comparison:

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact resistance｜wear resistant｜Toughening
  • Application Areas:Automotive sector｜Construction field
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA18 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA90 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-40°CISO 180/1A20 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A90 kJ/m²
flammabilityTest ConditionTest MethodTest Result
FMVSS flammabilityFMVSS302B
Flammability level1.5mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmUL 94HB
Burning rate1.00mmISO 379541 mm/min
mechanical propertiesTest ConditionTest MethodTest Result
bending strength3.5%StrainISO 17834.0 Mpa
Bending modulusISO 1781100 Mpa
Tensile creep modulus1000hrISO 899-1550 Mpa
Tensile creep modulus1hrISO 899-11100 Mpa
Nominal tensile fracture strainISO 527-2>50 %
Tensile strainYieldISO 527-230 %
tensile strengthYieldISO 527-241.0 Mpa
Tensile modulusISO 527-21400 Mpa
Friction coefficientvs.Itself-Dynamic,1hrASTM D18940.32
thermal performanceTest ConditionTest MethodTest Result
Glass transition temperatureISO 11357-2-35.0 °C
Melting temperatureISO 11357-3178 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A60.0 °C
Linear coefficient of thermal expansionMDISO 11359-21.3E-04 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-21.4E-04 cm/cm/°C
AnnealingTemperature160 °C
AnnealingTime-Optional30.0 min/mm
Effective thermal diffusivity coefficient6E-08 m²/s
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B100 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMDISO 294-41.3 %
Shrinkage rateTDISO 294-41.4 %
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 11331.70 cm3/10min
melt mass-flow rateISO 11332.0 g/10min
densityISO 11831.34 g/cm³
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.35 %
Water absorption rateSaturation,23°C,2.00mmISO 620.90 %
MediumDensity1.14 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexIEC 60112PLC 0
Relative permittivity1MHzIEC 602503.80
Relative permittivity100HzIEC 602504.40
Surface resistivityIEC 600931E+14 ohms
Volume resistivityIEC 600931E+14 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-SaleISO 2039-258
Rockwell hardnessR-SaleISO 2039-2105
Supplementary InformationTest ConditionTest MethodTest Result
EmissionVDA275<8.00 mg/kg
EmissionofOrganicCompoundsVDA2772.90 µgC/g
SpecificWear-AgainstASTM D189460.0 10^-6mm³/N·m
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.