PPA Zytel® HTN51G35EF DUPONT USA

243

Unit Price:US$ 5,317 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
77.9MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Thermal stability｜High temperature resistance｜Hydrolysis resistance
Application Areas:Automotive interior parts｜Fitness equipment｜electrical equipment
Color:--
Grade:Food grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS flammability		FMVSS302	B
Extreme Oxygen Index		ISO 4589-2	24 %
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	0.9mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	0.9mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	23 mm/min

mechanical properties	Test Condition	Test Method	Test Result
Poisson's ratio		ISO 527	0.39
bending strength		ISO 178	300 Mpa
Bending modulus		ISO 178	10300 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	2.4 %
tensile strength	Break	ISO 527-2	210 Mpa
Tensile modulus		ISO 527-2	12000 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	284 °C
Melting temperature		ISO 11357-3	300 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	5.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
SpecificHeatCapacity of Melt			1860 J/kg/°C
Shrinkage rate	MD	ISO 294-4	0.20 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.60 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	4.5 %
ThermalConductivityofMelt			0.25 W/m/K

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	-- ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	36 KV/mm
Relative permittivity	100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.00

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale	ISO 2039-2	124
Rockwell hardness	Rockwell hardness	M-Sale	ISO 2039-2	108

Supplementary Information	Test Condition	Test Method	Test Result
Odor		VDA270	4.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPA Zytel® HTN51G35EF DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet