PA66

PA66 Leona™ CR302 ASAHI JAPAN

211

Unit Price:US$ 3,318 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:wear resistant｜Electrical performance
Application Areas:Switch panel｜Insulation material
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
purpose			自动车电装部件
characteristic			电气特性

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	湿		1.4 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield，23°C	ASTM D638	128 Mpa
Elongation at Break	23°C	ASTM D638	3.0 %
bending strength	23°C	ASTM D790	191 Mpa
Bending modulus	23°C	ASTM D790	8800 Mpa
bending strength	干(湿)	ASTM D-790	191(157) Mpa
Elongation at Break	干(湿)	ASTM D-638	3(3.5) %
Rockwell hardness	干(湿)	ASTM D-785	90(-) R scale
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	36(39) J/m
flexural coefficient	干(湿)	ASTM D-790	8.8(5.8) GPa
tensile strength	干(湿)	ASTM D-638	128(98) Mpa
bending strength		ASTM D790/ISO 178	191(MPa) kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTM D790/ISO 178	8830(MPa) kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	M90
Impact strength of cantilever beam gap	23°C	ASTM D256	36.0 J/m

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.46MPa,干	ASTM D-648	250 °C
	Hot deformation temperature	1.82MPa,干	ASTM D-648	245 °C
	Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	245 ℃（℉）
Combustibility (rate)		UL 94	HB
Hot deformation temperature	0.45MPaUnannealed	ASTM D648	250 °C
Hot deformation temperature	Hot deformation temperature	1.80MPaUnannealed	ASTM D648	245 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	(23°C,50RH)	ASTM D570	1.4 %
Shrinkage rate	TD	ASTM D995	1.0 %
	Shrinkage rate	MD	ASTM D995	0.50 %
	Shrinkage rate	Shrinkage rate	干	旭化成方法	0.5-1.0 %
Water absorption rate		ASTM D570/ISO 62	1.4 %
Shrinkage rate		ASTM D955	0.5-1.0 %
density		ASTM D792/ISO 1183	1.52

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	90 M（Scale）

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Leona™ CR302 ASAHI JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet