Material Properties:Dimensional stability｜Low friction coefficient｜high strength｜Arc resistance｜Anti gamma radiation｜Easy to process｜Creep resistance｜Antichemical｜Low shrinkage｜Flame retardant
Application Areas:Electrical components｜Electrical appliances｜Military applications｜Laptop case｜Electronic field｜Electrical field
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

Other performance	Test Condition	Test Method	Test Result
combustibility		GB/T 2408-1996	FV-0 级

Mechanical properties	Test Method	Test Result
Shrinkage rate	GB/T 15585-1995	%
compressive strength	GB/T 1041-1992	MPa
Rockwell hardness	GB/T 9342-1988	hr
tensile strength	GB/T 1040-1992	MPa
elongation	GB/T 1040-1992	%
Flexural modulus	GB/T 9341-2000	MPa
bending strength	GB/T 9341-2000	172 MPa
Impact strength of cantilever beam gap	GB/T 1843-1996	KJ/m
elongation at break	ASTM D638/ISO 527	1.8 %
tensile strength	ASTM D638/ISO 527	120 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	ASTM D785	100
Flexural modulus	ASTM D790/ISO 178	1.15*100000 kg/cm²(MPa)[Lb/in²]
bending strength	ASTM D790/ISO 178	172 kg/cm²(MPa)[Lb/in²]

Electrical performance	Test Method	Test Result
dielectric constant	GB/T 1409-1988	MHz
dielectric strength	GB/T 1408.1-1999	kV/mm
Volume resistivity	GB/T 1410-1989	Ω.M
Surface Resistivity	GB/T 1410-1989	Ω

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.51

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		GB/T 1634.2-2004	℃
melting temperature			281 ℃（℉）

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.