Mechanical properties	Test Method	Test Result
Impact strength of cantilever beam gap	ASTM D256/ISO 179	28 kg·cm/cm(J/M)ft·lb/in
elongation at break	ASTM D638/ISO 527	8 %
tensile strength	ASTM D638/ISO 527	34 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	ASTM D785	95
Flexural modulus	ASTM D790/ISO 178	1500 kg/cm²(MPa)[Lb/in²]
tensile strength	ISO 527-2	34 Mpa
elongation	ISO 527-2	8 %
Rockwell hardness	ISO 2039-2	95 R
Flexural modulus	ISO 178	1500 Mpa
Impact strength of cantilever beam gap	ISO 180	28 J/m

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	0.9
melt mass-flow rate		ASTM D1238/ISO 1133	25 g/10min

Thermal performance	Test Method	Test Result
Heat distortion temperature	ASTM D648/ISO 75	85 ℃（℉）
melting temperature		163 ℃（℉）
vicat	ASTM D1525/ISO R306	154 ℃（℉）
Heat distortion temperature	ISO 75-2/B	85 °C
vicat	ISO 306/A50	154 °C
melting temperature	ISO 3146	163 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.