thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 3.20 mm	ASTM D648	123 °C
	Heat Deflection Temperature	0.45 MPa, 未退火, 6.40 mm	ASTM D648	129 °C
		Heat Deflection Temperature	1.8 MPa, 未退火, 3.20 mm	ASTM D648	107 °C
		Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm	ASTM D648	110 °C
vicat		ASTM D15254	129 °C
Linear coefficient of thermal expansion	流动 : -20 到 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : -20 到 150°C	ASTM E831	7.2E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.20 W/m/K
RTI Elec		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI		UL 746	60.0 °C

optical performance	Test Condition	Test Method	Test Result
gloss	60°, 无织构	ASTM D523	30

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Dart impact	-30°C, Total Energy	ASTM D3763	33.0 J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	40.0 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	17 g/10 min
shrinkage rate	流动 : 3.20 mm	内部方法	0.50 - 0.70 %
shrinkage rate	shrinkage rate	横向流动 : 3.20 mm	内部方法	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.10 %
Water absorption rate	Water absorption rate	平衡, 23°C	ASTM D570	0.40 %

Electrical performance	Test Method	Test Result
arc resistance	ASTM D495	PLC 6
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 2
High arc combustion index (HAI)	UL 746	PLC 0
Hot wire ignition (HWI)	UL 746	PLC 2

injection	Test Condition	Test Method	Test Result
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.040 %
Suggested injection volume			30 to 80 %
Temperature at the rear of the barrel			250 to 290 °C
Temperature in the middle of the barrel			255 to 295 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			275 to 300 °C
Processing (melt) temperature			275 to 300 °C
mold temperature			60 to 90 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服	ASTM D638	54.0 Mpa
elongation	断裂	ASTM D638	75 %
flexural modulus	50.0 mm 跨距	ASTM D790	2300 Mpa
bending strength	屈服, 50.0 mm 跨距	ASTM D790	84.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.