Material Properties:Flame retardant｜Filler: Mineral filler｜filler｜Mineral filler
Application Areas:Electrical applications｜Computer components｜OA device｜Business equipment｜OA device｜Business equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.2mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.8mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	3300	Mpa
tensile strength	Yield	ISO 527-2/50	62.0	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	48.0	Mpa
Tensile strain	Yield	ISO 527-2/50	2.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	30	%
Bending modulus		ISO 178	3200	Mpa
bending strength		ISO 178	96.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	91.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0	°C
Vicat softening temperature		ISO 306/B50	94.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:4.00mm	Internal Method	0.40-0.60	%
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.40-0.60	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.