Material Properties:Thermal stability｜High crystallinity｜Filler: Glass fiber reinforced material｜15% filler by weight
Application Areas:Automotive components｜Industrial machinery
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
MeltViscosity		ISO 11443	300000 mPa·s
Shrinkage rate		ISO 294-4	1.2 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.70 %
Water absorption rate		ISO 62	7.5 %
Water absorption rate	Water absorption rate		ISO 62	2.4 %

flammability	Test Method	Test Result
burning rate	ISO 3795	<100 mm/min
Limiting Oxygen Index	ISO 4589-2	25 %
FMVSS flammability	FMVSS302	B

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	80 kJ/m²

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	5000 Mpa
tensile strength	ISO 527-2	100 Mpa
Tensile strain	ISO 527-2	5.0 %
Poisson's ratio	ISO 527	--

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dissipation Factor		IEC 60250	0.016
Dissipation Factor	Dissipation Factor		IEC 60250	0.016
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	215 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	190 °C
Glass Transition Temperature		ISO 11357-2	60.0 °C
melting temperature		ISO 11357-3	221 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.