Material Description
- Material Properties:Middle flow｜Short molding cycle｜Good ductility
- Application Areas:Electronic and Electrical Applications｜Plastic bag
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 7.5 g/10 min | |
| Melt volume flow rate | ISO 1133 | 6.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.20 - 0.60 % | |
| 内部方法 | 0.20 - 0.60 % | ||
| Water absorption rate | ISO 62 | 0.15 % | |
| ISO 62 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3950 Mpa | |
| ISO 527-2/1 | 3900 Mpa | ||
| tensile strength | ASTM D638 | 55.0 Mpa | |
| ISO 527-2/5 | 54.0 Mpa | ||
| ASTM D638 | 45.0 Mpa | ||
| ISO 527-2/5 | 48.0 Mpa | ||
| elongation | ASTM D638 | 4.3 % | |
| ISO 527-2/5 | 4.3 % | ||
| ASTM D638 | 14 % | ||
| ISO 527-2/5 | 8.7 % | ||
| Flexural modulus | ASTM D790 | 3500 Mpa | |
| ISO 178 | 3450 Mpa | ||
| bending strength | ISO 178 | 98.0 Mpa | |
| ASTM D790 | 103 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 15 kJ/m² | |
| ISO 179/1eA | 25 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Dart impact | ASTM D3763 | 40.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 290 to 310 °C | ||
| Temperature in the middle of the barrel | 300 to 320 °C | ||
| Temperature at the front of the material cylinder | 310 to 330 °C | ||
| Spray nozzle temperature | 305 to 325 °C | ||
| Processing (melt) temperature | 310 to 330 °C | ||
| Temperature | 80 to 115 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 137 °C | |
| ISO 75-2/Ae | 135 °C | ||
| vicat | ASTM D152510 | 146 °C | |
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 4.7E-5 cm/cm/°C | |
| ASTM E831 | 7.0E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.