plas

PC/ABS MOCREATE® DCM01-4100 NINGBO ZHETIE DAFENG

242
  • Unit Price:US$ 1,857 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    40MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High temperature resistanceEasy electroplating
  • Application Areas:Automotive sector
  • Color:--
  • Grade:Electroplating grade

Technical Data Sheet

otherTest ConditionTest MethodTest Result
characteristic耐高温;易电镀
Color本色
purpose汽车领域
machinabilityTest ConditionTest MethodTest Result
Processing temperature210-240 °C
Processing temperature230-270 °C
Processing temperature230-260 °C
Processing temperature220-260 °C
Mold temperature50-90 °C
pressure30-80 Mpa
pressure40-120 Mpa
mechanical propertiesTest ConditionTest MethodTest Result
Elongation at BreakASTM D638/ISO 52750 %
tensile strengthASTM D638/ISO 52750 kg/cm²(MPa)[Lb/in²]
Bending modulusASTM D790/ISO 1782200 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 17880 kg/cm²(MPa)[Lb/in²]
thermal performanceTest ConditionTest MethodTest Result
Combustibility (rate)UL 94HB
Hot deformation temperatureHDTASTM D648/ISO 7594 ℃(℉)
Hot deformation temperatureHDTASTM D648/ISO 75115 ℃(℉)
Vicat softening temperatureASTM D1525/ISO R306110 ℃(℉)
Physical propertiesTest ConditionTest MethodTest Result
densityASTM D792/ISO 11831.1
Shrinkage rateASTM D9550.5-0.7 %
melt mass-flow rateASTM D1238/ISO 113327 g/10min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.