PA66

PA66 Zytel® 70G35HSLRA4 BK267 DUPONT USA

235

Unit Price:US$ 3,671 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜wear resistant
Application Areas:Electronic appliances｜Home appliance components｜Laptop case
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	6.00 J
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.70mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	21 %
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	5E-04 g
Burning rate	1.00mm	ISO 3795	18 mm/min
UL flame retardant rating	0.70mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	11000 Mpa
tensile strength	Break	ISO 527-2	210 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
bending strength		ISO 178	300 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	255 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Vicat softening temperature		ISO 306/B50	255 °C
Melting temperature		ISO 11357-3	260 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2.2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	1.4E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：--	ISO 11359-2	6.9E-05 cm/cm/°C
				Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	6.2E-05 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.4E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.40 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	5.5 %
MediumDensity			1.27 g/cm³
Top out temperature			210 °C
SpecificHeatCapacity of Melt			2300 J/kg/°C
ThermalConductivityofMelt			0.22 W/m/K
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.7 %

Electrical performance	Test Method	Test Result
Surface resistivity	IEC 60093	-- ohms
Volume resistivity	IEC 60093	1E+15 ohms·cm
Compared to the anti leakage trace index	IEC 60112	PLC 1

Supplementary Information	Test Condition	Test Method	Test Result
Odor		VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 70G35HSLRA4 BK267 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet