PC Makrolon® FR6005 901510 COVESTRO SHANGHAI

523

Unit Price:US$ 2,824 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
154.6MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to demould｜Impact resistance｜Aging resistance
Application Areas:Electronic and electrical enclosure
Color:--
Grade:--

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	0mm/min	ISO 527	2300	Mpa
tensile strength	Yield,50mm/min	ISO 527	62	Mpa
tensile strength	tensile strength	Break50mm/min	ISO 527	66	Mpa
elongation	Yield,50mm/min	ISO 527	6	%
Elongation at Break	50mm/min	ISO 527	50	%
Elongation at Break	Elongation at Break	50mm/min	ISO 527	135	%
bending strength	2.0mm/min	ISO 178	90	Mpa
Bending modulus	2.0mm/min	ISO 178	2400	Mpa
Impact strength of cantilever beam gap	23°C	ISO 180	60	kJ/m²
	Impact strength of cantilever beam gap	23°C	ISO 180	50	kJ/m²
		Impact strength of cantilever beam gap	23°C	ISO 180	15	kJ/m²
			Impact strength of cantilever beam gap	23°C	ISO 179	68	kJ/m²
				Impact strength of cantilever beam gap	23°C	ISO 179	50	kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 179	20	kJ/m²
Maximum puncture resistance at 23 ° C		ISO 6603	5100	N
Maximum puncture resistance -30 ° C		ISO 6603	6100	N
Puncture resistance	23℃	ISO 6603	54	J
Puncture resistance	Puncture resistance	-30℃	ISO 6603	55	J
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa	ISO 75	121	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa	ISO 75	136	°C
Vicat softening temperature	50°C/hr50N	ISO 306	142	°C
Vicat softening temperature	Vicat softening temperature	120°C/hr50N	ISO 306	144	°C
Linear coefficient of thermal expansion	Flow, 23~55℃	ISO 11359	0.000070	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂直, 23~55℃	ISO 11359	0.000070	cm/cm/°C
Ball indentation test		ISO 11359-2	134	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1200	kg/m3
Shrinkage rate	Flow	ISO 2577	0.6-0.8	%
Shrinkage rate	Shrinkage rate		ISO 2577	0.6-0.8	%
melt mass-flow rate	300°C1.2kg	ISO 1133	9	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	90000000000000000	Ω.m
Surface resistivity		IEC 60093	400000000000000000	Ω
CTI solution A		IEC 60112	200	V
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.0mm	UL 94	V-0
		UL flame retardant rating	1.2mm	UL 94	V-0
			UL flame retardant rating	1.2mm	UL 94	V-1
				UL flame retardant rating	1.5mm	UL 94	V-0
				UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Glow wire ignition temperature (GWIT)	1.0mm	ISO 11359-2	875	°C
	Glow wire ignition temperature (GWIT)	1.5mm	ISO 11359-2	850	°C
	Glow wire ignition temperature (GWIT)	Glow wire ignition temperature (GWIT)	3.0mm	ISO 11359-2	900	°C
Relative temperature of heating wire	1.0mm	ISO 11359-2	850	°C
	Relative temperature of heating wire	1.5mm	ISO 11359-2	960	°C
	Relative temperature of heating wire	Relative temperature of heating wire	3.0mm	ISO 11359-2	960	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.