Material Description

Material Properties:High gloss｜Aging resistance｜wear resistant｜Weather resistance｜Thermal stability
Application Areas:Casters｜Automotive sector｜Household appliances｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTMD542	1.586
transmissivity	2540μm	ASTM D1003	88.0to90.0	%
turbidity	2540μm	ASTM D1003	<0.80	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	65.0	J
-30°C		ISO 180/1U	无断裂
23°C		ASTMD4812	无断裂
23°C	23°C		ISO 180/1A	70	kJ/m²
-30°C		ISO 180/1A	12	kJ/m²
23°C		ASTM D256	700	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.50mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
crack		ISO 527-2/50	>70	%
50.0mm span		ASTM D790	2300	Mpa
--7		ISO 178	2300	Mpa
--8		ISO 178	90.0	Mpa
crack		ASTM D638	>70	%
yield		ISO 527-2/50	6.0	%
	yield		ASTM D638	6.0	%
		yield		ISO 527-2/50	63.0	Mpa
		yield	yield		ASTM D638	63.0	Mpa
--2		ASTM D638	2350	Mpa
Yield, 50.0mm span		ASTM D790	90.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
1.8MPa, unannealed, 3.20mm		ASTM D648	124	°C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	135	°C
0.45MPa, unannealed, 3.20mm		ASTM D648	135	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	124	°C
Vicat softening temperature		ISO 527-3/1	141	°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
-40 to 95 ° C		ASTME831	7E-05	cm/cm/°C
23 to 80 ° C		ISO 11359-2	7E-05	cm/cm/°C
thermal conductivity		DENKA Method	0.20	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Balance, 23 ° C		ASTM D570	0.35	%
Saturation, 23 ° C		ISO 62	0.35	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD：--1	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	17.0	cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	18	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	60Hz	ASTMD150	1E-03
Dissipation factor	Dissipation factor	1MHz	ASTMD150	0.010
Volume resistivity		ASTMD257	>1.0E+15	ohms·cm
Dielectric strength	1.60mm	ASTM D2863	27	KV/mm
Dielectric constant	60Hz	ASTMD150	3.00
Dielectric constant	Dielectric constant	1MHz	ASTMD150	3.00
hardness	Test Condition	Test Method	Test Result	Test Unit
Hardness (Rockwell R)		ISO 2039-2	120
Hardness (Rockwell R)	Hardness (Rockwell R)		ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.