PC/PTFE LNP™ LUBRILOY™ D20001-8T8D029L SABIC INNOVATIVE US
312
- Unit Price:US$ 8,736 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:wear resistant
- Application Areas:Electrical appliances｜Plastic bag｜Aerospace Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ASTM D1238 | 15.7 cm3/10min | |
| Shrinkage rate | ASTM D955 | 0.50 % | |
| ASTM D955 | 0.60 % | ||
| ISO 294-4 | 0.57 % | ||
| ISO 294-4 | 0.53 % | ||
| Water absorption rate | ISO 62 | 0.12 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2550 Mpa | |
| ISO 527-2/1 | 2600 Mpa | ||
| tensile strength | ASTM D638 | 67.0 Mpa | |
| ISO 527-2 | 62.0 Mpa | ||
| ASTM D638 | 60.0 Mpa | ||
| ISO 527-2 | 54.0 Mpa | ||
| elongation | ASTM D638 | 4.5 % | |
| ISO 527-2 | 4.3 % | ||
| ASTM D638 | 6.5 % | ||
| ISO 527-2 | 6.7 % | ||
| Flexural modulus | ASTM D790 | 2820 Mpa | |
| ISO 178 | 2800 Mpa | ||
| bending strength | ASTM D790 | 103 Mpa | |
| ISO 178 | 102 Mpa | ||
| coefficient of friction | ASTM D3702 | 0.090 | |
| ASTM D3702 | 0.22 | ||
| Wear factor | ASTM D3702 | 6.0E+6 10^-8 mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 1600 J/m | |
| ISO 180/1U | 100 kJ/m² | ||
| Dart impact | ASTM D3763 | 51.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature at the rear of the barrel | 250 to 260 °C | ||
| Temperature in the middle of the barrel | 255 to 265 °C | ||
| Temperature at the front of the material cylinder | 260 to 270 °C | ||
| Processing (melt) temperature | 255 to 290 °C | ||
| Temperature | 40 to 65 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| screw speed | 30 to 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 97.0 °C | |
| ASTM D648 | 89.0 °C | ||
| ISO 75-2/Af | 94.0 °C | ||
| Linear coefficient of thermal expansion | ASTM E831 | 6.6E-5 cm/cm/°C | |
| ASTM E831 | 6.7E-5 cm/cm/°C | ||
| ISO 11359-2 | 6.7E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.