PA66 Akulon® N-252-UX62 MITSUBISHI ENGINEERING JAPAN
201
- Unit Price:US$ 3,552 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low temperature resistance｜wear resistant｜Filler: Glass mineral｜25% filler by weight
- Application Areas:Automotive components｜Electronic and electrical components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 236 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 227 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 4E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 31 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 6E+15 ohms·cm | |
| dielectric strength | 1.00mm | IEC 60243-1 | 21 KV/mm |
| relative permittivity | 100Hz | IEC 60250 | 5.00 |
| 1MHz | IEC 60250 | 5.00 | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.011 |
| 1MHz | IEC 60250 | 8E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Surface Resistivity | IEC 60093 | 4E+15 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 2.6 g/10min |
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 1.90 cm3/10min |
| shrinkage rate | 0.45 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.24 % |
| 平衡,23°C,50%RH | ISO 62 | 1.1 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 25700 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 174 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 11 % |
| flexural modulus | ISO 178 | 21900 Mpa | |
| bending strength | ISO 178 | 289 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.