Material Description

Material Properties:Flame retardant｜High temperature resistance｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Electronic and electrical components
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	kJ/m²	40
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	kJ/m²	40

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		%	35 --
Hot filament ignition temperature	0.400mm	°C	725 --
Burning wire flammability index	0.400mm	°C	960 --
Flammability level	1.50mm		V-0 --
Flammability level	Flammability level	0.750mm		V-0 --

mechanical properties	Test Condition	Test Method	Test Result
bending strength		MPa	215 180
Bending modulus		MPa	7800 8200
Tensile strain	Break	%	2.4 2.2
tensile strength	Break		135 MPa
Tensile modulus			8200 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:55to160°C	cm/cm/°C	1E-04 --
	Linear coefficient of thermal expansion	TD:-40to23°C	cm/cm/°C	6.4E-05 --
		Linear coefficient of thermal expansion	TD	cm/cm/°C	6.8E-05 --
			Linear coefficient of thermal expansion	MD:55to160°C	cm/cm/°C	2.1E-05 --
				Linear coefficient of thermal expansion	MD:-40to23°C	cm/cm/°C	2.7E-05 --
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	cm/cm/°C	2.5E-05 --
Melting temperature		°C	310 --
Hot deformation temperature	1.8MPa,Unannealed	°C	276 --

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	%	1.1 --
Shrinkage rate	Shrinkage rate	MD	%	0.30 --

Electrical performance	Test Method	Test Result
Compared to the anti leakage trace index	V	PLC 0
Dielectric strength	kV/mm	42 --
Volume resistivity	ohms·cm	>1.0E+15 --

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® HTNFR52G20LX NC010 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet