PA66 Zytel® 77G43L-BK031 DUPONT USA

159

Unit Price:US$ 5,668 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength
Application Areas:Automotive components｜Electronic and Electrical Applications
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R 计秤	ISO 2039-2	118

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	217 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	203 °C
Glass Transition Temperature		ISO 11357-2	65.0 °C
melting temperature		ISO 11357-3	218 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	1.4E-5 cm/cm/°C
	Linear coefficient of thermal expansion	流动 : -40 到 23°C	ISO 11359-2	2.1E-5 cm/cm/°C
		Linear coefficient of thermal expansion	流动 : 55 到 160°C	ISO 11359-2	1.3E-5 cm/cm/°C
			Linear coefficient of thermal expansion	横向	ISO 11359-2	1.1E-4 cm/cm/°C
				Linear coefficient of thermal expansion	横向 : -40 到 23°C	ISO 11359-2	7.5E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 55 到 160°C	ISO 11359-2	1.4E-4 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
burning rate	1.00 mm	ISO 3795	21 mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
FMVSS combustion rate		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	1.0E-4 g

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²

Filling analysis	Test Condition	Test Method	Test Result
Ejection Temperature			210 °C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量	ISO 294-4	0.80 %
shrinkage rate	shrinkage rate	流量	ISO 294-4	0.30 %
Water absorption rate	饱和, 23°C, 2.00 mm	ISO 62	1.7 %
Water absorption rate	Water absorption rate	平衡, 23°C, 2.00 mm, 50% RH	ISO 62	0.70 %
viscosity number		ISO 307	145 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 62631-3-1	1.0E+13 ohms·m

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			280 to 300 °C
Melt Temperature, Optimum			290 °C
mold temperature			70 to 120 °C
Mold Temperature, Optimum			100 °C
pressure holding			50.0 to 100 Mpa
pressure holding	pressure holding	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	12500 Mpa
tensile strength	断裂	ISO 527-2	200 Mpa
Tensile strain	断裂	ISO 527-2	3.0 %
flexural modulus		ISO 178	11000 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.