Material Properties:enhance｜High mobility｜Flame retardant｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Fiber grade
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	146 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	143 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	6.2E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-0

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	50 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2kg	ISO 1133	8.5 g/10min
Melt volume flow rate	300°C/1.2kg	ISO 1133	8.00 cm3/10min
shrinkage rate	TD:3.20mm		0.30-0.50 %
shrinkage rate	shrinkage rate	MD:3.20mm		0.10-0.30 %
Water absorption rate	饱和,23°C	ISO 62	0.11 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 4

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	6500 Mpa
tensile strength	断裂	ISO 527-2	97.0 Mpa
Tensile strain	断裂	ISO 527-2	2.7 %
flexural modulus		ISO 178	5900 Mpa
bending strength		ISO 178	160 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.