PA66

PA66 Leona™ CR301 BK ASAHI JAPAN

253

Unit Price:US$ 3,727 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:dimensional stability ｜Conductive
Application Areas:Electrical components｜Electrical field｜Electronic field｜Switch panel｜Industrial applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	51 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Taber abraser	1000 Cycles	ASTM D1044	-- mg
bending strength	23°C	ISO 178	140 Mpa
bending strength	bending strength	--	ASTM D790	147 Mpa
Bending modulus	23°C	ISO 178	7400 Mpa
Bending modulus	Bending modulus	--	ASTM D790	5900 Mpa
elongation	Break, 23°C	ISO 527-2	2.0 %
elongation	elongation	Break	ASTM D638	3.0 %
tensile strength	--	ASTM D638	88.0 Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2	85.0 Mpa
Tensile modulus	23°C	ISO 527-2	7000 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow	ASTM D696	4.0E-5 cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	249 °C
	Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	250 °C
		Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	188 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	191 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	-- %
Water absorption rate	Water absorption rate	Saturation, 23°C		-- %
Shrinkage rate	Flow	Internal Method	0.50 - 1.3 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale	ISO 2039-2	85
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	85

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Leona™ CR301 BK ASAHI JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet