PC LEXAN™ 243R-111L SABIC INNOVATIVE NANSHA
170
- Unit Price:US$ 2,767 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Industrial applications｜Automotive sector｜Electrical appliances｜Lighting applications｜Plastic bag
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ASTM D785 | 118 |
| M计秤 | ASTM D785 | 70 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| refractive index | ASTM D542 | 1.586 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| vicat | ASTM D15255 | 154 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 132 °C |
| 0.45MPa,未退火,6.40mm | ASTM D648 | 138 °C | |
| RTI Str | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C | |
| thermal conductivity | ASTMC177 | 0.27 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 25 % | |
| UL flame retardant rating | 6.0mm | UL 94 | V-0 |
| 0.75mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² | |
| 23°C | ASTM D4812 | 3200 J/m | |
| 23°C | ASTM D256 | 800 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Outdoor applicability | UL 746C | f1 | |
| Water absorption rate | 平衡,100°C | ASTM D570 | 0.58 % |
| density | ASTM D792 | 1.19 g/cm³ | |
| ASTM D792 | 1.20 g/cm³ | ||
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 平衡,23°C | ASTM D570 | 0.35 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric constant | 1MHz | ASTM D150 | 2.96 |
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| dielectric constant | 60Hz | ASTM D150 | 3.17 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 |
| Dissipation Factor | 60Hz | ASTM D150 | 9E-04 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.1 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| 断裂 | ASTM D638 | 110 % | |
| tensile strength | 屈服 | ASTM D638 | 62.1 Mpa |
| 断裂 | ASTM D638 | 65.5 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.