PBT VALOX™ ENH4560 BK1066 SABIC INNOVATIVE NANSHA
184
- Unit Price:US$ 6,887 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Bromine free｜Chlorine free
- Application Areas:Plastic bag｜Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 142 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 140 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 223 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 225224 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 210 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 210 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| MD:23到150°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| TD:-40到40°C | ISO 11359-2 | 6.2E-05 cm/cm/°C | |
| TD:23到150°C | ISO 11359-2 | 1.5E-04 cm/cm/°C | |
| RTI Elec | UL 746 | 140 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL 94 | V-0 |
| 3.00mm | UL 94 | 5VB | |
| Burning wire flammability index | 2.00mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 750 °C |
| 2.00mm | IEC 60695-2-13 | 750 °C | |
| 3.00mm | IEC 60695-2-13 | 800 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler | ASTM D229 | 30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ISO 180/1A | 9.0 kJ/m² | |
| -30°C | ASTM D4812 | 500 J/m | |
| 23°C | ASTM D4812 | 500 J/m | |
| -30°C | ISO 180/1U | 37 kJ/m² | |
| 23°C | ISO 180/1U | 37 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/2U | 35 kJ/m² |
| 23°C | ISO 179/2U | 40 kJ/m² | |
| -30°C | ASTM D256 | 75 J/m | |
| 0°C | ASTM D256 | 75 J/m | |
| 23°C | ASTM D256 | 75 J/m | |
| -30°C | ISO 180/1A | 9.0 kJ/m² | |
| 0°C | ISO 180/1A | 9.0 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 110 Pa·s |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 23 g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 16.0 cm3/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 1MHz | ASTMD150 | 3.80 |
| Dissipation Factor | 1MHz | ASTMD150 | 0.14 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| IEC 60112 | V | ||
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTMD257 | 1E+14 ohms·cm | |
| 0.800mm, inoil | ASTM D149 | 32 KV/mm | |
| 16mm, inoyl | ASTM D149 | 22 KV/mm | |
| 3.20mm, inoil | ASTM D149 | 18 KV/mm | |
| 0.800mm, In oil | IEC 60243-1 | 32 KV/mm | |
| 1.60mm, In oil | IEC 60243-1 | 22 KV/mm | |
| 3.20mm, In oil | IEC 60243-1 | 18 KV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 11000 Mpa | |
| yield | ASTM D638 | 110 Mpa | |
| ISO 527-2/5 | 105 Mpa | ||
| fracture | ASTM D638 | 110 Mpa | |
| Fracture bending strain | ISO 178 | 2.0 % | |
| fracture | ISO 527-2/5 | 105 Mpa | |
| yield | ASTM D638 | 2.0 % | |
| ISO 527-2/5 | 2.0 % | ||
| fracture | ASTM D638 | 2.0 % | |
| ISO 527-2/5 | 2.0 % | ||
| 50.0mm span | ASTM D790 | 9000 Mpa | |
| --7 | ISO 178 | 10000 Mpa | |
| --8 | ISO 178 | 170 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 150 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 150 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.