PA66 Vydyne®  66B ASCEND USA

271
  • Unit Price:US$ 3,613 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    48MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:--

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexASTM D286328 %
Hot filament ignition temperature3.0 mmIEC 60695-2-13700 °C
Hot filament ignition temperature1.5 mmIEC 60695-2-13700 °C
Hot filament ignition temperature0.71 mmIEC 60695-2-13700 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Burning wire flammability index1.5 mmIEC 60695-2-12850 °C
Burning wire flammability index0.71 mmIEC 60695-2-12850 °C
UL flame retardant rating3.0 mmUL 94V-2
UL flame retardant rating1.5 mmUL 94HB
UL flame retardant rating0.71 mmUL 94HB
squeeze outTest ConditionTest MethodTest Result
Melt Temperature270 to 295 °C
Oral mold temperature270 to 295 °C
Temperature in Zone 5 of the material cylinder250 to 295 °C
Temperature in Zone 4 of the material cylinder250 to 295 °C
Temperature in Zone 3 of the material cylinder250 to 295 °C
Temperature in Zone 2 of the material cylinder250 to 295 °C
Temperature in Zone 1 of the material cylinder250 to 295 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-2/1A2800 Mpa
tensile strengthYield, 23°CISO 527-2/1A85.0 Mpa
tensile strengthBreak, 23°CISO 527-2/1A55.0 Mpa
Tensile strainYield, 23°CISO 527-25.0 %
Nominal tensile fracture strain23°CISO 527-2/1A> 25 %
Bending modulus23°CISO 1783100 Mpa
bending strength23°CISO 17890.0 Mpa
Poisson's ratio23°CISO 527-20.42
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B195 °C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/A70.0 °C
Melting temperatureISO 11357-3260 °C
Linear coefficient of thermal expansionFlow : 23 to 55°C, 2.00 mmISO 11359-21.0E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 55°C, 2.00 mmISO 11359-21.0E-4 cm/cm/°C
RTI Elec0.71 mmUL 746130 °C
RTI Elec1.5 mmUL 746130 °C
RTI Elec3.0 mmUL 746130 °C
RTI Imp0.71 mmUL 74675.0 °C
RTI Imp1.5 mmUL 74675.0 °C
RTI Imp3.0 mmUL 74675.0 °C
RTI0.71 mmUL 74685.0 °C
RTI1.5 mmUL 74685.0 °C
RTI3.0 mmUL 74685.0 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate横向Flow : 2.00 mmISO 294-42.0 %
Shrinkage rateFlow : 2.00 mmISO 294-42.1 %
Water absorption rateSaturation, 23°CISO 628.5 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 622.5 %
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strength1.00 mmIEC 6024326 KV/mm
Hot wire ignition3.0 mmUL 746PLC 2
Hot wire ignition1.5 mmUL 746PLC 3
Hot wire ignition0.71 mmUL 746PLC 4
High voltage arc tracing rateUL 746PLC 0
High arc combustion index3.0 mmUL 746PLC 0
High arc combustion index1.5 mmUL 746PLC 0
High arc combustion index0.71 mmUL 746PLC 0
Compared to the anti leakage trace index3.00 mmIEC 60112 V
Arc resistance3.00 mmASTM D495PLC 5
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.