Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Automotive Applications｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.0 kJ/m²
-30°C		ASTM D256	35 J/m
23°C		ASTM D256	32 J/m
-30°C		ISO 180/1A	2.0 kJ/m²
23°C		ISO 180/1A	2.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	48.0 J

mechanical properties	Test Condition	Test Method	Test Result
yield		ASTM D638	7.0 %
yield	yield		ISO 527-2/5	7.0 %
crack		ASTM D638	80 %
crack	crack		ISO 527-2/5	80 %
50.0mm span		ASTM D790	3320 Mpa
--7		ISO 178	3100 Mpa
--8		ISO 178	135 Mpa
Yield, 50.0mm span		ASTM D790	145 Mpa
--1		ASTM D638	3210 Mpa
yield		ASTM D638	103 Mpa
yield	yield		ISO 527-2/5	98.0 Mpa
crack		ASTM D638	85.0 Mpa
crack	crack		ISO 527-2/5	80.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
1.8MPa, unannealed, 3.20mm		ASTM D648	173 °C
1.8MPa, unannealed, 6.40mm		ASTM D648	178 °C
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	168 °C
Flow: -40 to 150 ° C	-40to150°C	ASTME831	6E-05 cm/cm/°C
Flow: 23 to 150 ° C	23to150℃	ISO 11359-2	5.5E-05 cm/cm/°C
Horizontal: -40 to 150 ° C	Across Flow, -40to150°C	ASTME831	6E-05 cm/cm/°C
Horizontal: 23 to 150 ° C	Across Flow, 23to150℃	ISO 11359-2	5.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	56.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Saturation,23°C	ISO 62	0.36 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %
melt mass-flow rate	337°C/6.6kg	ASTM D1238	43 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ DT1810EV-1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet