PC LEXAN™ 4704 SABIC INNOVATIVE US
125
- Unit Price:US$ 5,045 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:24MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜Middle flow
- Application Areas:Electrical applications｜Lighting applications｜Automotive Applications
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 2.0 g/10min | |
| Melt volume flow rate | ISO 1133 | 2.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.80-1.0 % | |
| 24hr | ASTM D570 | 0.19 % | |
| Saturation, 23 ° C | ISO 62 | 0.16 % | |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 92 | |
| ASTM D785 | 127 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.600 | |
| transmissivity | ASTM D1003 | 85.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3029 | 149 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 578 kJ/m² | |
| -30°C | ASTM D256 | 84 J/m | |
| 23°C | ASTM D256 | 370 J/m | |
| -30°C | ISO 180/1A | 6.0 kJ/m² | |
| 23°C | ISO 180/1A | 7.0 kJ/m² | |
| Suspended wall beam without notch impact strength | ASTM D4812 | 3200 J/m | |
| Dart impact | ASTM D3763 | 74.0 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 50.0mm span | ASTM D790 | 2330 Mpa | |
| --7 | ISO 178 | 2070 Mpa | |
| --8 | ISO 178 | 66.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 97.2 Mpa | |
| --1 | ASTM D638 | 2080 Mpa | |
| yield | ASTM D638 | 65.5 Mpa | |
| ISO 527-2/50 | 68.0 Mpa | ||
| fracture | ASTM D638 | 77.9 Mpa | |
| ISO 527-2/50 | 68.0 Mpa | ||
| yield | ASTM D638 | 8.0 % | |
| ISO 527-2/50 | 7.0 % | ||
| fracture | ASTM D638 | 78 % | |
| ISO 527-2/50 | 100 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | 1.6E-03 | |
| ASTM D150 | 1.6E-03 | ||
| ASTM D150 | 0.026 | ||
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 3 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| Volume resistivity | ASTM D257 | >2.5E+17 ohms·cm | |
| dielectric strength | ASTM D149 | 20 KV/mm | |
| dielectric constant | ASTM D150 | 3.27 | |
| ASTM D150 | 3.27 | ||
| ASTM D150 | 3.10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 149 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 150 °C | |
| Flow: -40 to 40 ° C | ASTME831 | 6E-05 cm/cm/°C | |
| Flow: -40 to 95 ° C | ASTME831 | 8.1E-05 cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 6E-05 cm/cm/°C | |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.21 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.