PEI ULTEM™  HU1000 7H4D017USDD SABIC INNOVATIVE US

261
  • Unit Price:US$ 18,663 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Middle flow｜Biocompatibility｜Steam sterilization
  • Application Areas:Medical devices｜Medical and nursing supplies
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap23°CISO 180/1A6.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA4.0 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexASTM D286347 %
NBSSmokeDensity-Flaming,Ds,4minASTME6620.700
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6383580 Mpa
Tensile modulusISO 527-2/13200 Mpa
tensile strengthYieldASTM D638110 Mpa
tensile strengthYieldISO 527-2/5105 Mpa
tensile strengthBreakASTM D63890.0 Mpa
bending strengthYield,50.0mmSpanASTM D790173 Mpa
bending strengthISO 178160 Mpa
Bending modulusISO 1783300 Mpa
Bending modulus50.0mmSpanASTM D7903440 Mpa
Tensile strainBreakISO 527-2/560 %
elongationBreakASTM D63860 %
Tensile strainYieldISO 527-2/56.0 %
elongationYieldASTM D6387.0 %
tensile strengthBreakISO 527-2/585.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperature--ISO 306/B120211 °C
Vicat softening temperature--ISO 306/B50215 °C
Vicat softening temperatureASTM D152510219 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af215 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648201 °C
Linear coefficient of thermal expansionMD：-20to150°CASTME8315.6E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-25E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-20to150°CASTME8315.4E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-25E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 620.70 %
Water absorption rateEquilibrium,23°CASTM D5701.3 %
Water absorption rateSaturation,23°CISO 621.3 %
Water absorption rate24hrASTM D5700.25 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Melt Volume Flow Rate (MVR)220°C/5.0kgISO 113313.0 cm3/10min
melt mass-flow rate337°C/6.6kgASTM D12389.0 g/10min
Electrical performanceTest ConditionTest MethodTest Result
Arc resistanceASTM D495PLC 5
Compared to the anti leakage trace indexCTIUL 746PLC 4
High arc combustion indexHAIUL 746PLC 3
High voltage arc tracing rateHVTRUL 746PLC 2
Hot wire ignitionHWIUL 746PLC 1
Volume resistivityASTM D2571E+17 ohms·cm
Dielectric strength1.60mm,inAirASTM D14933 KV/mm
Dielectric strength1.60mm,in OilASTM D14928 KV/mm
Dielectric constant1kHzASTM D1503.15
Dissipation factor1kHzASTM D1501.3E-03
Dissipation factor2.45GHzASTM D1502.5E-03
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.