POM

POM TENAC™-C 8520 ASAHI JAPAN

267

Unit Price:US$ 3,294 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:Industrial applications｜Household goods｜Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			汽车部件.齿轮.控制杆等。

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238	45 g/10min
melt mass-flow rate	melt mass-flow rate	190℃/2.16kg	ISO 1133	45 g/10min
Water absorption rate	24 hr	ASTM D570	0.2 %

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ASTM D790	2630 MPa
Impact strength of cantilever beam gap		ASTM D256	39 J/m
Tensile modulus		ISO 527-2	2900 MPa
Tensile stress	Yield	ISO 527-2	67 MPa
tensile strength		ASTM D638	61 MPa
elongation	Break	ASTM D638	45 %
Impact strength of cantilever beam gap		ASTM D256/ISO 179	39 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	61 kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	40 %
Bending modulus		ASTM D790/ISO 178	2630 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	90 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,unannealed	ASTM D648	158 ℃
	Hot deformation temperature	0.45MPa,unannealed	ISO 75-2/B	156 ℃
	Hot deformation temperature	Hot deformation temperature	1.8MPa,unannealed	ISO 75-2/A	105 ℃
Linear coefficient of thermal expansion	Flow	ASTM E831	0.0001 cm/cm/℃
UL flame retardant rating		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	110 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow	ASTM D955	1.6-2 %
Shrinkage rate	Shrinkage rate	Across Flow	ISO 294-4	1.6-2 %
Rockwell hardness	R-Scale	ASTM D785	115
density		ASTM D792/ISO 1183	1.41
Shrinkage rate		ASTM D955	1.6-2.0 %
melt mass-flow rate		ASTM D1238/ISO 1133	70 g/10min
Water absorption rate		ASTM D570/ISO 62	0.2 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM TENAC™-C 8520 ASAHI JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet