mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	0.060MPa,0.15m/sec7	JISK7218	4000	10^-8mm³/N·m
Tensile modulus		ISO 527-2	2250	Mpa
tensile strength		ISO 527-2	54.0	Mpa
Nominal tensile fracture strain		ISO 527-2	20	%
Bending modulus		ISO 178	2100	Mpa
bending strength		ISO 178	72.0	Mpa
Friction coefficient	Dynamic2	JISK7218	0.38
Friction coefficient	Friction coefficient	Steel - Dynamic3	JISK7218	0.75
Wear factor	0.49MPa,0.30m/sec4	JISK7218	<1.0	10^-8mm³/N·m
	Wear factor	0.49MPa,0.30m/sec5	JISK7218	600	10^-8mm³/N·m
	Wear factor	Wear factor	0.060MPa,0.15m/sec6	JISK7218	1500	10^-8mm³/N·m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ISO 1133	19	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	18.0	cm3/10min
Water absorption rate	23°C,24hr	ISO 62	0.50	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	5E+15	ohms
Volume resistivity		IEC 60093	7E+13	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	80
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			CF2001

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.