PPO NORYL™ GFN30F-873S SABIC INNOVATIVE SHANGHAI

Unit Price:US$ 3,900 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Shanghai port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Junlong Plastic & Chemical Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Hydrolysis resistance
Application Areas:Automotive components｜Laptop case
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	20.0	J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	590	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C8	ISO 180/1U	30	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break3	ASTM D638	3.0	%
elongation	elongation	Break	ISO 527-2/50	2.5	%
tensile strength	Break	ISO 527-2/50	110	Mpa
tensile strength	tensile strength	Break3	ASTM D638	130	Mpa
Tensile modulus	--	ISO 527-2/1	8200	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	8600	Mpa
Bending modulus	50.0 mm Span4	ASTM D790	7200	Mpa
Bending modulus	Bending modulus	--5	ISO 178	6800	Mpa
bending strength	--5,6	ISO 178	160	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	160	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature at the rear of the barrel			265 to 315	°C
Suggested injection volume			30 to 70	%
Suggested maximum moisture content			0.020	%
drying time			3.0 to 4.0	hr
drying temperature			110 to 120	°C
Temperature in the middle of the barrel			275 to 320	°C
Temperature at the front of the material cylinder			290 to 325	°C
Spray nozzle temperature			300 to 325	°C
Processing (melt) temperature			300 to 325	°C
Mold temperature			80 to 110	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			20 to 100	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	2.3E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	2.1E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	149	°C
Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	147	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	139	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	147	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.040	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.10	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.10 - 0.40	%
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	2.00	cm3/10min
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	3.2	g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 4160 /MT

Supplier Join

Get App

Top

PPO NORYL™ GFN30F-873S SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials