Material Properties:Thermal stability｜wear resistant｜High temperature resistance｜currency
Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances｜Automotive sector
Color:--
Grade:Demoulding grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.5	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2750	Mpa
tensile strength		ISO 527-2	65.0	Mpa
Tensile strain	Yield	ISO 527-2	10	%
Tensile strain	Tensile strain	Break	ISO 527-2	35	%
Bending modulus		ISO 178	2550	Mpa
bending strength		ISO 178	87.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	100	°C
Melting temperature		ISO 11357-3	165	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.41	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	9.0	g/10min
Shrinkage rate	MD：3.00mm	Internal Method	2.0	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
Dielectric strength		IEC 60243-1	19	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.