PC/ABS

PC/ABS CYCOLOY™ CY4000 7M1D052L SABIC INNOVATIVE NANSHA

273

Unit Price:US$ 2,836 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high strength｜Aging resistance
Application Areas:Electronic and electrical accessories｜Shell
Color:--
Grade:Injection grade

Technical Data Sheet

UL	Test Condition	Test Method	Test Result
UL flame retardant rating	2.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
RTI Elec	2.5mm	UL 746B	60 °C
RTI Elec	RTI Elec	3.0mm	UL 746B	60 °C
RTI Imp	2.5mm	UL 746B	60 °C
RTI Imp	RTI Imp	3.0mm	UL 746B	60 °C
RTI Str	2.5mm	UL 746B	60 °C
RTI Str	RTI Str	3.0mm	UL 746B	60 °C

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23℃	ISO 180	10 kJ/m²
Bending modulus	23℃	ISO 178	2500 Mpa
bending strength	Yield23℃	ISO 178	85 Mpa
elongation	23℃	ISO 527	40 %
elongation	elongation	Yield23℃ 50mm/min	ISO 527	3 %
tensile strength	23℃ 50mm/min	ISO 527	45 Mpa
tensile strength	tensile strength	Yield23℃	ISO 527	55 Mpa
Tensile modulus	23℃	ISO 527	2700 Mpa
Linear coefficient of thermal expansion	垂直	ISO 11359	0.000080 cm/cm/℃
Vicat softening temperature	120℃/hr 50N	ISO 306	90 °C
Vicat softening temperature	Vicat softening temperature	50℃/hr 50N	ISO 306	85 °C
Hot deformation temperature	Unannealed1.8MPa	ISO 75	72 °C
Hot deformation temperature	Hot deformation temperature	Unannealed0.45MPa	ISO 75	85 °C
Taber wear resistance	1kg		15 mg/1000cy
Charpy Notched Impact Strength	-30℃	ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	10 kJ/m²
Impact strength of cantilever beam gap	-30℃	ISO 180	10 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260℃ 2.16kg	ISO 1133	21 g/10min
melt mass-flow rate	melt mass-flow rate	260℃ 2.16kg	ASTM D1238	23 g/10min
Shrinkage rate		ISO 294	0.6 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294	0.4 %
density		ISO 1183	1.2 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1000000000000000
Dielectric strength	3.2mm	IEC 60243	17 KV/mm
Dielectric constant	1MHz	IEC 60250	2.7
Volume resistivity		IEC 60093	1000000000000000 Ω.cm
Dielectric constant		IEC 60250	2.7
Dispersion factor 1MHz		IEC 60250	0.006
Dissipation factor		IEC 60250	0.006
Compared to the anti leakage trace index		IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039	110 Mpa

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating	2.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Relative temperature of heating wire	3.2mm	IEC 60695	960 °C
Extreme Oxygen Index		ISO 4589	29 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLOY™ CY4000 7M1D052L SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet