ABS Toyolac® 440Y TORAY JAPAN

301

Unit Price:US$ 3,592 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting
Application Areas:Industrial machinery｜Fitness equipment
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	16	kJ/m²
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	98	J/m
	Impact strength of cantilever beam gap	-30°C,12.7mm	ASTM D256	91	J/m
		Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	210	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	160	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	44.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	54.0	Mpa
elongation	Break	ASTM D638	15	%
Tensile strain	Break,23°C	ISO 527-2	12	%
Bending modulus		ASTM D790	2500	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2470	Mpa
bending strength		ASTM D790	77.0	Mpa
bending strength	bending strength	23°C	ISO 178	82.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	95.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	92.0	°C
Vicat softening temperature			100	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.06	g/cm³
density	density	23°C	ISO 1183	1.06	g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	10	g/10min
Shrinkage rate		Internal Method	0.50-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	115
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ISO 2039-2	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.