ABS TR-530F LG CHEM KOREA

219

Unit Price:US$ 3,090 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting
Application Areas:Automotive Applications
Color:--
Grade:Transparent level

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity		ASTM D1003	3.0	%
transmissivity		ASTM D1003	89.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C, 6.40 mm, Injection	ASTM D256	240	J/m
	Impact strength of cantilever beam gap	23°C, 3.20 mm, Injection	ASTM D256	90	J/m
		Impact strength of cantilever beam gap	-30°C, 6.40 mm, Injection	ASTM D256	90	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C, 3.20 mm, Injection	ASTM D256	240	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C, 3.20 mm, Injection	ASTM D790	49.0	Mpa
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	1500	Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	> 15	%
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	33.0	Mpa
Tensile modulus	23°C, 3.20 mm, Injection	ASTM D638	1350	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Mold temperature			40 to 60	°C
Back pressure			30.0 to 60.0	Mpa
Screw speed			30 to 80	rpm
Processing (melt) temperature			210 to 240	°C
Spray nozzle temperature			210 to 240	°C
Temperature at the front of the material cylinder			210 to 230	°C
Temperature in the middle of the barrel			200 to 220	°C
Temperature at the rear of the barrel			190 to 210	°C
drying time			2.0 to 4.0	hr
drying temperature			80 to 90	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D15255	81.0	°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	74.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.40 - 0.70	%
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	10	g/10 min
density	比重	ASTM D792	1.06	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	88

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Xinlin	US$ 3580 /MT

Supplier Join

Get App

Top