Material Properties:wear resistant
Application Areas:Electrical appliances｜Electronic and Electrical Applications｜Plastic bag｜Industrial applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D955	2.0-2.2 %
	Shrinkage rate		ASTM D955	2.0-2.2 %
		Shrinkage rate		ISO 294-4	2.0-2.2 %
		Shrinkage rate	Shrinkage rate		ISO 294-4	2.0-2.2 %
Water absorption rate		ASTM D570	0.23 %
Water absorption rate	Water absorption rate		ISO 62	0.37 %

Mechanical properties	Test Condition	Test Method	Test Result
elongation		ASTM D638	11 %
Tensile strain		ISO 527-2	9.4 %
Flexural modulus		ASTM D790	2620 Mpa
Flexural modulus	Flexural modulus		ISO 178	2900 Mpa
bending strength		ASTM D790	86.0 Mpa
bending strength	bending strength		ISO 178	86.5 Mpa
coefficient of friction		ASTM D3702Modified	0.23
coefficient of friction	coefficient of friction		ASTM D3702Modified	0.091
Wear factor		ASTM D3702Modified	12.0 10^-10in^5-min/ft-lb-hr
Tensile modulus		ASTM D638	2550 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2700 Mpa
tensile strength		ASTM D638	56.1 Mpa
tensile strength	tensile strength		ISO 527-2	50.6 Mpa

Impact resistance	Test Method	Test Result
Impact strength of cantilever beam gap	ISO 180/1A	4.5 kJ/m²
Suspended wall beam without notch impact strength	ISO 180/1U	39 kJ/m²
Dart impact	ASTM D3763	7.20 J
Multi axis Instrumented Impact Energy	ISO 6603-2	0.960 J

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	95.0 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	98.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.