Material Properties:High rigidity｜High impact｜Filler: Glass fiber reinforced material｜45% filler by weight
Application Areas:Electronic and Electrical Applications｜Automotive sector
Color:--
Grade:UV resistant grade

Technical Data Sheet Compare

physical property	Test Method	Test Result
melt mass-flow rate	ISO 1133	13 g/10min
Melt volume flow rate	ISO 1133	8.50 cm3/10min
Shrinkage rate		0.32 %
Water absorption rate	ISO 62	0.73 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	16000 Mpa
tensile strength	ISO 527-2	208 Mpa
Tensile strain	ISO 527-2	2.0 %
Flexural modulus	ISO 178	14300 Mpa
bending strength	ISO 178	349 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	90 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
relative permittivity		IEC 60250	4.10
Dissipation Factor		IEC 60250	5.5E-03
Dissipation Factor	Dissipation Factor		IEC 60250	6.7E-03
relative permittivity		IEC 60250	4.20

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	232 °C
Glass Transition Temperature		ISO 11357-2	87.0 °C
melting temperature		ISO 11357-3	257 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	5.6E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.