PC INFINO® CF-3300HF K2115 LOTTE KOREA

306

Unit Price:US$ 3,460 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant｜Filler: Glass fiber reinforced material｜Filler: Glass fiber reinforced material
Application Areas:Phone
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	18	kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	180	J/m
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	150	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	17	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	V-1
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ASTM D638	120	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	125	Mpa
elongation	Break	ASTM D638	3.8	%
Tensile strain	Break	ISO 527-2/50	3.8	%
Bending modulus		ASTM D790	6500	Mpa
Bending modulus	Bending modulus		ISO 178	7300	Mpa
bending strength		ASTM D790	170	Mpa
bending strength	bending strength		ISO 178	180	Mpa
Tensile modulus		ASTM D638	6400	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	6900	Mpa
tensile strength	Yield	ASTM D638	120	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	125	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	143	°C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	143	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	140	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	138	°C
Vicat softening temperature	--	ISO 306/B50	147	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	148	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	250°C/10.0kg	ASTM D1238	22	g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ISO 1133	22	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.10-0.30	%
	Shrinkage rate	TD：3.20mm	ASTM D955	0.10-0.30	%
		Shrinkage rate	TD:3.20mm	ISO 2577	0.10-0.30	%
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.10-0.30	%
density		ASTM D792	1.40	g/cm³
density	density		ISO 1183	1.40	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	115
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Sihao Industrial	US$ 3970 /MT

Supplier Join

Get App

Top

PC INFINO® CF-3300HF K2115 LOTTE KOREA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index