PC LEXAN™ EXL1414-BK10227L SABIC INNOVATIVE US
163
- Unit Price:US$ 2,840 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
- Application Areas:Bottle cap｜Home appliance components｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | L 计秤 | ASTM D785 | 89 |
| R 级 | ASTM D785 | 121 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 125 °C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 139 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距9 | ISO 75-2/Be | 140 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 124 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9 | ISO 75-2/Ae | 128 °C | |
| vicat | -- | ASTM D152510 | 145 °C |
| -- | ISO 306/B120 | 146 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 875 °C |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 875 °C |
| UL flame retardant rating | 0.40 mm | UL 94 | HB |
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 850 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| 23°C | ISO 179/1eA | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 770 J/m |
| 23°C | ASTM D256 | 870 J/m | |
| -30°C8 | ISO 180/1A | 60 kJ/m² | |
| 23°C8 | ISO 180/1A | 70 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 70.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| mold temperature | 70 to 95 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| drying temperature | 120 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 100 Hz | ASTM D150 | 1.2E-3 |
| 1 MHz | ASTM D150 | 9.3E-3 | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| dielectric strength | 0.800 mm, in Oil | ASTM D149 | 16 KV/mm |
| dielectric constant | 100 Hz | ASTM D150 | 2.68 |
| 1 MHz | ASTM D150 | 2.64 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | -- | ASTM D792 | 1.18 g/cm³ |
| -- | ISO 1183 | 1.19 g/cm³ | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2020 Mpa |
| -- | ISO 527-2/1 | 2150 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 55.0 Mpa |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| 断裂3 | ASTM D638 | 50.0 Mpa | |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 6.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂3 | ASTM D638 | 98 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2230 Mpa |
| --5 | ISO 178 | 2250 Mpa | |
| bending strength | --5,6 | ISO 178 | 85.0 Mpa |
| 屈服, 50.0 mm 跨距4 | ASTM D790 | 92.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.