GPPS POLYREX® PG-22 TAIWAN CHIMEI

354

Unit Price:US$ 1,837 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
GPPS POLYREX® PG-22 ZHENJIANG CHIMEI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜transparent｜high strength
Application Areas:Food service sector
Color:--
Grade:Injection grade

Material Certification

MSDS

RoHS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179	2.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	1.8 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	2.0 kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	1.8 kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	14 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	15 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2/50	40.0 Mpa
elongation	Break	ASTM D638	2.0 %
Tensile strain	Break	ISO 527-2/50	3.0 %
Bending modulus		ASTM D790	3030 Mpa
tensile strength	Break	ASTM D638	41.6 Mpa
bending strength		ISO 178	54.0 Mpa
bending strength	bending strength		ASTM D790	52.9 Mpa
Bending modulus		ISO 178	2400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	5.0E-5to8.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	82.0 °C
	Vicat softening temperature	--	ISO 306/A50	87.0 °C
	Vicat softening temperature	Vicat softening temperature		ASTM D15256	87.0 °C
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	79.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	73.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	75.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.40-0.70 %
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	18.8 cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	18 g/10min
density	23°C	ISO 1183	1.04 g/cm³
density	density	比重	ASTM D792	1.05 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	74

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.