PC PANLITE® ML-3120ZHP TEIJIN JAPAN
303
- Unit Price:US$ 4,406 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:18.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜transparent
- Application Areas:Casters｜Fitness equipment
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 高光扩散 | ||
| Color | 半透明 | ||
| purpose | LED灯管.LED面板灯 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 129 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ | |
| Heat Deflection Temperature | 1.80MPa | ISO 75-1 | 129 °C |
| 阻燃性，1.0mm/3.0mm | UL 94 | V-2 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | 1.5mmt | JIS K7136 | 52 % |
| Pigment dispersion | 2.0mmt | In-house method | 60 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1200 | |
| Dissolving fingers | 300℃ | ISO 1133 | 8 cm310min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 20 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ASTM D638/ISO 527 | 66 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 61 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 96 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 120 % | |
| tensile strength | 50mm/min，屈服 | ISO 527-1 | 61 Mpa |
| 50mm/min，断裂 | ISO 527-1 | 65 Mpa | |
| Elongation at break | 50mm/min | ISO 527-1 | 120 % |
| flexural modulus | 2mm/min | ISO 178 | 2200 Mpa |
| bending strength | 2mm/min | ISO 178 | 95 Mpa |
| Impact strength of cantilever beam gap | Notched | ISO 179 | 20 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.