PC LEXAN™ 9925A-NA1A0036 SABIC INNOVATIVE US

246

Unit Price:US$ 2,531 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜Thermal stability
Application Areas:Electronic and electrical components｜Thin walled products｜Automotive sector
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	75.0	J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	68	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.50mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
--8		ISO 178	95.0	Mpa
Yield, 50.0mm span		ASTM D790	91.0	Mpa
--7		ISO 178	2240	Mpa
50.0mm span		ASTM D790	2150	Mpa
crack		ISO 527-2/50	77	%
crack	crack		ASTM D638	83	%
yield		ISO 527-2/50	6.0	%
yield	yield		ASTM D638	6.0	%
crack		ISO 527-2/50	56.0	Mpa
crack	crack		ASTM D638	60.0	Mpa
yield		ISO 527-2/50	62.0	Mpa
yield	yield		ASTM D638	60.0	Mpa
--1		ASTM D638	2300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05	cm/cm/°C
Vicat softening temperature		ASTM D152513	140	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	123	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	124	°C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	135	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
melt mass-flow rate	300°C/1.2kg	ASTM D1238	13	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.