ABS

ABS POLYLAC® PA-766 TAIWAN CHIMEI

382

Unit Price:US$ 3,697 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜heat-resisting｜High impact resistance
Application Areas:Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			难燃、耐热、高冲击

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638/ISO 527	370 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	95
Bending modulus		ASTM D790/ISO 178	2.0×104 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	8360 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	3.9 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	23 kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTM D-790	2.0×10 kg/cm
tensile strength		ASTM D-638	370 kg/cm
bending strength		ASTM D-790	8360 lb/in
Bending modulus		ASTM D-790	2.8×10 lb/in
Impact strength of cantilever beam gap	1/4〃	ASTM D-256	3.9 ft.lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/8"	ASTM D-256	23 kg.cm/cm
tensile strength		ASTM D-638	5250 lb/in
Impact strength of cantilever beam gap	1/8"	ASTM D-256	4.3 ft.lb/in
Rockwell hardness		ASTM D-785	95 R
elongation		ASTM D-638	30 %
bending strength		ASTM D-790	590 kg/cm
Impact strength of cantilever beam gap	1/4〃	ASTM D-256	21 kg.cm/cm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT	ASTM D648/ISO 75	89(192) ℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	98 ℃（℉）
Hot deformation temperature	HDT	ASTM D-648	89(192) °C
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D-648	81(178) ℉
Vicat softening temperature		ASTM D-1525	98 °C
Vicat softening temperature	Vicat softening temperature		ASTM D-1525	214 ℉
Combustibility	File No. E56070 UL&C-UL		1/16"V-0

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.20
melt mass-flow rate		ASTM D1238/ISO 1133	25 g/10min
	melt mass-flow rate	220℃×10kg	ASTM D-1238	25 g/10min
	melt mass-flow rate	melt mass-flow rate	200℃ 5kg	ASTM D-1238	2.3 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-766 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet