PC Makrolon® LQ3187 COVESTRO GERMANY
168
- Unit Price:US$ 3,152 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low viscosity
- Application Areas:Automotive Applications｜Electrical applications｜Industrial applications｜Safety equipment｜lens｜Optical applications｜glasses
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 116 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 137 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 125 °C | |
| Glass Transition Temperature | ISO 11357-2 | 145 °C | |
| vicat | -- | ISO 306/B50 | 146 °C |
| -- | ISO 306/B120 | 147 °C | |
| ball-indentation hardness | 137°C | IEC 60695-10-2 | Pass |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.586 | |
| transmissivity | 1000µm | ISO 13468-2 | 89.0 % |
| 2000µm | ISO 13468-2 | 89.0 % | |
| 3000µm | ISO 13468-2 | 88.0 % | |
| 4000µm | ISO 13468-2 | >85.0 % | |
| Haze ratio | 3000µm | ISO 14782 | 1.0 % |
| AbbeNumber | 30.0 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| FlashIgnitionTemperature | ASTM D1929 | 480 °C | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | 23°C | IEC 60426 | A1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 60.0 J |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 6500 N |
| 23°C | ISO 6603-2 | 5600 N | |
| Charpy Notched Impact Strength | -30°C,完全断裂 | ISO 7391 | 14 kJ/m² |
| 23°C,局部断裂 | ISO 7391 | 80 kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | NoBreak |
| -30°C | ISO 179/1eU | NoBreak | |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C,完全断裂 | ISO 7391 | 15 kJ/m² |
| 23°C,局部断裂 | ISO 7391 | 70 kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 70.0 J |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water Vapor Transmission Rate | 23°C,85%RH,100µm | ISO 15106-1 | 15 g/m²/24hr |
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO 2556 | 16900 cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO 2556 | 3800 cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO 2556 | 510 cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO 2556 | 120 cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO 2556 | 2760 cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO 2556 | 650 cm³/m²/bar/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 34 KV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 |
| 23°C,1MHz | IEC 60250 | 3.00 | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 5E-04 |
| 23°C,1MHz | IEC 60250 | 9.5E-03 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| 解决方案B | IEC 60112 | PLC 4 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD:2.00mm3 | ISO 294-4 | 0.70 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| 平衡,23°C,50%RH | ISO 62 | 0.12 % | |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Apparent density | ISO 60 | 0.66 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 6.5 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.00 cm3/10min |
| shrinkage rate | TD | ISO 2577 | 0.60-0.80 % |
| MD | ISO 2577 | 0.60-0.80 % | |
| TD:2.00mm3 | ISO 294-4 | 0.75 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile creep modulus | 1000hr | ISO 899-1 | 1900 Mpa |
| flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178 | 74.0 Mpa |
| 23°C | ISO 178 | 98.0 Mpa | |
| Bending Strain | 23°C | ISO 178 | 7.0 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 66.0 Mpa |
| 断裂,23°C | ISO 527-2/50 | 70.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 6.2 % |
| 断裂,23°C | ISO 527-2/50 | 120 % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 2200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.