PPO

PPO NORYL™  SE1GFN2 WH5D030 SABIC INNOVATIVE SHANGHAI

258
  • Unit Price:US$ 4,105 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhance｜Glass fiber reinforced
  • Application Areas:Electronic communication accessories｜Electronic communication accessories
  • Color:--
  • Grade:--

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact23°C, Total EnergyASTM D376318.0 J
Suspended wall beam without notch impact strength23°C8ISO 180/1U28 kJ/m²
Suspended wall beam without notch impact strength-30°C8ISO 180/1U27 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D4812520 J/m
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94V-1
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span5ASTM D790140 Mpa
bending strength--6,7ISO 178150 Mpa
Bending modulus--6ISO 1785600 Mpa
Bending modulus50.0 mm Span5ASTM D7905500 Mpa
elongationBreakISO 527-2/502.5 %
elongationBreak4ASTM D6383.0 %
tensile strengthBreakISO 527-2/50100 Mpa
tensile strengthBreak4ASTM D638120 Mpa
Tensile modulus--ISO 527-2/16400 Mpa
Tensile modulus--3ASTM D6387100 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature110 to 120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume30 to 70 %
Temperature at the rear of the barrel265 to 315 °C
Temperature in the middle of the barrel275 to 320 °C
Temperature at the front of the material cylinder290 to 325 °C
Spray nozzle temperature300 to 325 °C
Processing (melt) temperature300 to 325 °C
Mold temperature80 to 110 °C
Back pressure0.300 to 0.700 Mpa
Screw speed20 to 100 rpm
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8312.5E-5 cm/cm/°C
Vicat softening temperature--ISO 306/B120144 °C
Vicat softening temperature--ASTM D15259142 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8ISO 75-2/Af133 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648134 °C
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648142 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CISO 11359-23.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8317.5E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-27.5E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate24 hr, 23°C2ISO 620.040 %
Water absorption rate24 hr, 23°CISO 620.11 %
Shrinkage rate3.20 mm，FlowInternal Method0.20 - 0.50 %
Melt Volume Flow Rate (MVR)280°C/5.0 kgISO 11333.00 cm3/10min
melt mass-flow rate280°C/5.0 kgASTM D12383.5 g/10 min
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityASTM D2571.3E+17 ohms
Volume resistivityASTM D2572.0E+16 ohms·cm
Dielectric strength1.60 mm, in OilASTM D14926 KV/mm
Dielectric strength1.50 mm, in OilIEC 60243-126 KV/mm
Dielectric constant1 MHzASTM D1502.93
Dielectric constant1 MHzIEC 602502.90
Dissipation factor1 MHzASTM D1503.4E-3
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.