PA6 Durethan® BKV30F 000000 ENVALIOR WUXI
200
- Unit Price:US$ 2,978 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Heat aging
- Application Areas:Automotive connectors｜Automotive components｜Instrument accessories｜Electronic and Electrical Applications｜Communication equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 218 °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 204 °C | |
| Vicat softening temperature | ISO 306/B120 | 210 °C | |
| Melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO 11359-2 | 2.2E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 8.1E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 | |
| Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 960 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 775 °C |
| 1.5mm | IEC 60695-2-13 | 775 °C | |
| 3.0mm | IEC 60695-2-13 | 800 °C | |
| Extreme Oxygen Index | ISO 4589-2 | 32 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GFHR.14-110.GF30;ISO1043-PAGFFR(30+40+72) |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric strength | 23°C,1.00mm | IEC 60243-1 | 37 KV/mm |
| Compared to the anti leakage trace index | SolutionA | IEC 60112 | PLC 0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | 260°C/2.16kg | ISO 1133 | 23.0 cm3/10min |
| Shrinkage rate | TD:280°C,2.00mm2 | ISO 294-4 | 0.62 % |
| TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.18 % | |
| MD:280°C,2.00mm2 | ISO 294-4 | 0.22 % | |
| MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.080 % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 5.0 % |
| Equilibrium,23°C,50%RH | ISO 62 | 1.5 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Break,23°C | ISO 527-2/5 | 3.0 % |
| Bending modulus | 23°C | ISO 178/A | 9800 Mpa |
| bending strength | 3.5%Strain | ISO 178/A | -- Mpa |
| 23°C | ISO 178 | 210 Mpa | |
| FlexuralStrainatFlexuralStrength5(23°C) | 2.7 % | ||
| Tensile modulus | 23°C | ISO 527-2/1 | 10800 Mpa |
| tensile strength | Break,23°C | ISO 527-2/5 | 150 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.